This paper describes the development of two new grades of Fe-3Cr-3W(Mo) alloys at the Oak Ridge National Laboratory. The two grades are designated as A and B. The higher strength Grade B differs from Grade A in that it contains 0.10 wt % Ta. Both grades, when tested in normalized and tempered conditions, show a good combination of tensile strength and Charpy impact properties. Tensile properties of both A and B are over 150 MPa (20 ksi) higher than the highest strength commercial alloy T23. Grade B has higher creep-rupture strength than the T23 steel for the entire temperature range from 540 to 650°C. Grade B also exceeds creep-rupture strength of modified 9Cr-1Mo alloy (Grade 91) up to 615°C. Grade A exceeds the creep-rupture strength of T23 steel up to 600°C and match its values at the higher temperatures. Both grades have been scaled up to 50-ton-size commercial heats and processed into forgings and hot-rolled plates and bars.
- Pressure Vessels and Piping Division
Mechanical Properties of New Grades of FE-3Cr-W Alloys
- Views Icon Views
- Share Icon Share
- Search Site
Sikka, VK, Klueh, RL, Maziasz, PJ, Babu, S, Santella, ML, Jawad, MH, Paules, JR, & Orie, KE. "Mechanical Properties of New Grades of FE-3Cr-W Alloys." Proceedings of the ASME/JSME 2004 Pressure Vessels and Piping Conference. Experience With Creep-Strength Enhanced Ferritic Steels and New and Emerging Computational Methods. San Diego, California, USA. July 25–29, 2004. pp. 97-106. ASME. https://doi.org/10.1115/PVP2004-2576
Download citation file: