One of the most popular additive manufacturing processes is laser-based direct metal laser sintering (DMLS) process, which enables us to make complex three-dimensional (3D) parts directly from computer-aided design models. Due to layer-by-layer formation, parts built in this process tend to be anisotropic in nature. Suitable heat treatment can reduce this anisotropic behavior by changing the microstructure. Depending upon the applications, a wide range of mechanical properties can be achieved between 482 °C and 621 °C temperature for precipitation-hardened stainless steels. In the present study, effect of different heat treatment processes, namely solution annealing, aging, and overaging, on tensile strength, hardness, and wear properties has been studied in detail. Suitable metallurgical and mechanical characterization techniques have been applied wherever required, to support the experimental observations. Results show H900 condition gives highest yield strength and lowest tensile strain at break, whereas solution annealing gives lowest yield strength and as-built condition gives highest tensile strain at break. Scanning electron microscope (SEM) images show that H900 and H1150 condition produces brittle and ductile morphology, respectively, which in turn gives highest and lowest hardness value, respectively. X-ray diffraction (XRD) analysis shows presence of austenite phases, which can increase ductility at the cost of hardness. Average wear loss for H900 condition is highest, whereas it is lowest for solution annealed condition. Further optical and SEM images have been taken to understand the basic wear mechanism involved.
Skip Nav Destination
Article navigation
November 2017
Research-Article
Effect of Different Heat Treatments on Mechanical Properties of Laser Sintered Additive Manufactured Parts
Sagar Sarkar,
Sagar Sarkar
Department of Mechanical Engineering,
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: sagar.sarkar123@gmail.com
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: sagar.sarkar123@gmail.com
Search for other works by this author on:
Cheruvu Siva Kumar,
Cheruvu Siva Kumar
Department of Mechanical Engineering,
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: kumar@mech.iitkgp.ernet.in
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: kumar@mech.iitkgp.ernet.in
Search for other works by this author on:
Ashish Kumar Nath
Ashish Kumar Nath
Department of Mechanical Engineering,
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: aknath@mech.iitkgp.ernet.in
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: aknath@mech.iitkgp.ernet.in
Search for other works by this author on:
Sagar Sarkar
Department of Mechanical Engineering,
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: sagar.sarkar123@gmail.com
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: sagar.sarkar123@gmail.com
Cheruvu Siva Kumar
Department of Mechanical Engineering,
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: kumar@mech.iitkgp.ernet.in
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: kumar@mech.iitkgp.ernet.in
Ashish Kumar Nath
Department of Mechanical Engineering,
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: aknath@mech.iitkgp.ernet.in
Indian Institute of Technology Kharagpur,
Kharagpur 721302, West Bengal, India
e-mail: aknath@mech.iitkgp.ernet.in
1Corresponding author.
Manuscript received July 19, 2017; final manuscript received July 21, 2017; published online September 13, 2017. Editor: Y. Lawrence Yao.
J. Manuf. Sci. Eng. Nov 2017, 139(11): 111010 (11 pages)
Published Online: September 13, 2017
Article history
Received:
July 19, 2017
Revised:
July 21, 2017
Citation
Sarkar, S., Kumar, C. S., and Nath, A. K. (September 13, 2017). "Effect of Different Heat Treatments on Mechanical Properties of Laser Sintered Additive Manufactured Parts." ASME. J. Manuf. Sci. Eng. November 2017; 139(11): 111010. https://doi.org/10.1115/1.4037437
Download citation file:
Get Email Alerts
Arc characteristics of aluminum alloy double-wire high-frequency pulsed GMAW
J. Manuf. Sci. Eng
Gravitational Effects on Optical Lens Fabrication: First Insides on Earth- and Microgravity Experiments
J. Manuf. Sci. Eng (December 2024)
Related Articles
Mechanical Properties and Structure of Laser Beam and Wide Gap Brazed Joints Produced Using Mar M247–Amdry DF3 Powders
J. Eng. Gas Turbines Power (April,2019)
Laser Powder Bed Fusion Additive Manufacturing of Maraging Steel: A Review
J. Manuf. Sci. Eng (November,2023)
Effect of Post Heat Treatment on the Microstructure and Tensile Properties of Nano TiC Particulate Reinforced Inconel 718 by Selective Laser Melting
J. Manuf. Sci. Eng (May,2020)
Investigations on Additive Manufacturing of Ti–6Al–4V by Microplasma Transferred Arc Powder Deposition Process
J. Manuf. Sci. Eng (August,2018)
Related Proceedings Papers
Related Chapters
Introduction and Definitions
Handbook on Stiffness & Damping in Mechanical Design
Strain Hardening and Tensile Properties
New Advanced High Strength Steels: Optimizing Properties
Novel and Efficient Mathematical and Computational Methods for the Analysis and Architecting of Ultralight Cellular Materials and their Macrostructural Responses
Advances in Computers and Information in Engineering Research, Volume 2